The 357 an 45s were from 3% antimony "floor" shotand I had good bullets from no 1 in the pot warmed moulds . Upon reflection it my have been my alloy.I had some battery post and terminal stuff for decoyanchors that may have been the pan flat that I used . If that is what I did would that explain the results?